Annealing (metallurgy)
|
| |
|
| |
Annealing, in metallurgy and materials science, is a heat treatment wherein a material is altered, causing changes in its properties such as strength and hardness. It is a process that produces conditions by heating to above the re-crystallization temperature and maintaining a suitable temperature, and then cooling. Annealing is used to induce ductility, soften material, relieve internal stresses, refine the structure by making it homogeneous, and improve cold working properties.
In the cases of copper, steel, silver, and brass this process is performed by substantially heating the material (generally until glowing) for a while and allowing it to cool slowly.
Discussion
Ask a question about 'Annealing (metallurgy)' Start a new discussion about 'Annealing (metallurgy)' Answer questions from other users |
Encyclopedia
Annealing, in metallurgy and materials science, is a heat treatment wherein a material is altered, causing changes in its properties such as strength and hardness. It is a process that produces conditions by heating to above the re-crystallization temperature and maintaining a suitable temperature, and then cooling. Annealing is used to induce ductility, soften material, relieve internal stresses, refine the structure by making it homogeneous, and improve cold working properties.
In the cases of copper, steel, silver, and brass this process is performed by substantially heating the material (generally until glowing) for a while and allowing it to cool slowly. In this fashion the metal is softened and prepared for further work such as shaping, stamping, or forming. It also presents no problem with decarburization.
Thermodynamics of annealing
Annealing occurs by the diffusion of atoms within a solid material, so that the material progresses towards its equilibrium state. Heat is needed to increase the rate of diffusion by providing the energy needed to break bonds. The movement of atoms has the effect of redistributing and destroying the dislocations in metals and (to a lesser extent) in ceramics. This alteration in dislocations allows metals to deform more easily, so increases their ductility.
The amount of process-initiating Gibbs free energy in a deformed metal is also reduced by the annealing process. In practice and industry, this reduction of Gibbs free energy is termed "stress relief".
The relief of internal stresses is a thermodynamically spontaneous process; however, at room temperatures, it is a very slow process. The high temperatures at which the annealing process occurs serve to accelerate this process.
The reaction facilitating the return of the cold-worked metal to its stress-free state has many reaction pathways, mostly involving the elimination of lattice vacancy gradients within the body of the metal. The creation of lattice vacancies are governed by the Arrhenius equation, and the migration/diffusion of lattice vacancies are governed by Fick’s laws of diffusion.
Mechanical properties, such as hardness and ductility, change as dislocations are eliminated and the metal's crystal lattice is altered. On heating at specific temperature and cooling it is possible to bring the atom at the right lattice site and new grain growth can improve the mechanical properties.
Stages of annealing
There are three stages in the annealing process, with the first being the recovery phase, which results in softening of the metal through removal of crystal defects (the primary type of which is the linear defect called a dislocation) and the internal stresses which they cause. Recovery phase covers all annealing phenomena that occur before the appearance of new strain-free grains. The second phase is recrystallization, where new strain-free grains nucleate and grow to replace those deformed by internal stresses. If annealing is allowed to continue once recrystallization has been completed, grain growth will occur, in which the microstructure starts to coarsen and may cause the metal to have less than satisfactory mechanical properties.
Annealing in a controlled atmosphere
The low temperature of annealing (about 50 °F above C3 line) may result in oxidation of the metal’s surface, resulting in scale. If scale is to be avoided, annealing is carried out in an oxygen-, carbon-, and nitrogen-free atmosphere (to avoid oxidation, carburization, and nitriding respectively) such as endothermic gas (a mixture of carbon monoxide, hydrogen gas, and nitrogen).
The magnetic properties of mu-metal (Espey cores) are introduced by annealing the alloy in a hydrogen atmosphere.
Setup and Equipment
Typically, large ovens are used for the annealing process. The inside of the oven is large enough to place the workpiece in a position to receive maximum exposure to the circulating heated air. For high volume process annealing, gas fired conveyor furnaces are often used. For large workpieces or high quantity parts Car-bottom furnaces will be used in order to move the parts in and out with ease. Once the annealing process has been successfully completed, the workpieces are sometimes left in the oven in order for the parts to have a controled cooling process. While some workpieces are left in the oven to cool in a controled fashion, other materials and alloys are removed from the oven. After being removed from the oven, the workpieces are often quickly cooled off in a process known as quench hardening. Some typical methods of quench hardening materials involve the use of mediums such as air, water, oil, or salt.
Diffusion annealing of semiconductors
In the semiconductor industry, silicon wafers are annealed, so that dopant atoms, usually boron, phosphorus or arsenic, can diffuse into substitutional positions in the crystal lattice, resulting in drastic changes in the electrical properties of the semiconducting material.
Specialized annealing cycles
Normalization
Normalization is an annealing process in which a metal is cooled in air after heating.
This process is typically confined to hardenable steel. It is used to refine grains which have been deformed through cold work, and can improve ductility and toughness of the steel. It involves heating the steel to just above its upper critical point. It is soaked for a short period then allowed to cool in air. Small grains are formed which give a much harder and tougher metal with normal tensile strength and not the maximum ductility achieved by annealing.
Process annealing
Process annealing, also called "intermediate annealing", "subcritical annealing", or "in-process annealing", is a heat treatment cycle that restores some of the ductility to a work piece allowing it be worked further without breaking. Ductility is important in shaping and creating a more refined piece of work through processes such as rolling, drawing, forging, spinning, extruding and heading. The piece is heated to a temperature typically below the austenizing temperature, and held there for long enough to relieve stresses in the metal. The piece is finally cooled slowly in to room temperature. It is then ready again for additional cold working. This can also be used to ensure there is reduced risk of distortion of the work piece during machining, welding, or further heat treatment cycles.
The temperature range for process annealing is ranges from 500 °F to 1400 °F, depending on the alloy in question.
Full anneal
A full anneal typically results in the most ductile state a metal can assume for metal alloy. It creates an entirely new homogeneous and uniform structure with good dynamic properties. To perform a full anneal, a metal is heated to its annealing point (about 50°C above the austenic temperature as graph shows) and held for sufficient time to allow the material to fully austenitize, to form austenite or austenite-cementite grain structure. The material is then allowed to cool slowly so that the equilibrium microstructure is obtained. In some cases this means the material is allowed to air cool. In other cases the material is allowed to furnace cool. The details of the process depend on the type of metal and the precise alloy involved. In any case the result is a more ductile material that has greater stretch ratio and reduction of area properties but a lower yield strength and a lower tensile strength. This process is also called LP annealing for lamellar pearlite in the steel industry as opposed to a process anneal which does not specify a microstructure and only has the goal of softening the material. Often material that is annealed will be machined and then be followed by further heat treatment to obtain the final desired properties.
Short cycle anneal
Short cycle annealing is used for turning normal ferrite into malleable ferrite. It consists of heating, cooling, and then heating again from 4 to 8 hours.
See also
External links
- : Ameritherm offers annealing overview and Application Notes
- :efunda - engineering fundamentals
- :Material Science
|
| |
|
|